Kinetics of defect recovery and long-range ordering in Ni₃Al + B - I. Simultaneous recovery and ordering in cold-rolled material

Autor(en)

W. Pfeiler, R. Kozubski, H. P. Karnthaler, C. Rentenberger

Abstrakt

Defect recovery and long-range ordering (LRO) during isochronal annealing of cold-rolled Ni₇₆Al₂₄+ 0.19 at.% B (400 wt ppm) were studied by residual resistometry, transmission electron microscopy (TEM) and microhardness tests. The cold-rolling causes a decrease of the degree of LRO and an effective increase of the mobility of vacancies. The long-range ordering process during isochronal annealing proceeds, however, qualitatively in a similar way both in as-rolled and in homogenised samples. TEM observations revealed two stages of the defect recovery. Firstly, superlattice intrinsic stacking faults (SISF) of large density recovered almost completely in the temperature regime between 443 and 700 K showing that they are bounded by dislocations of opposite sign. Secondly, the recovery of antiphase-boundary (APB) dissociated superlattice dislocations occurred by the annihilation of dipoles within the whole temperature regime leading finally to a loss of all dislocations at 1273 K.

Organisation(en)

Dynamik Kondensierter Systeme, Physik Nanostrukturierter Materialien

Externe Organisation(en)

Jagiellonian University in Krakow

Journal

Acta Materialia

Band

44

Seiten

1563-1571

Anzahl der Seiten

9

ISSN

1359-6454

DOI

https://doi.org/10.1016/1359-6454(95)00276-6

Publikationsdatum

01-1996

Peer-reviewed

Ja

ÖFOS 2012

103018 Materialphysik, 103042 Elektronenmikroskopie

ASJC Scopus Sachgebiete

Electronic, Optical and Magnetic Materials, Ceramics and Composites, Polymers and Plastics, Metals and Alloys

Link zum Portal

https://ucrisportal.univie.ac.at/de/publications/kinetics-of-defect-recovery-and-longrange-ordering-in-ni3al--b--i-simultaneous-recovery-and-ordering-in-coldrolled-material(ec9f4a21-1f58-4a18-b36c-e29adc57f71f).html